FARCO LEVEL FLEX is a high modulus, moisture curing, self leveling, and one component sealant based on polyurethane.
ASTM C 920 , TYPE S, GRADE P, CLASS 25
TT- S – 00230 C , TYPE I , CLASS A
ISO 11600 –F-25LM
Consistency Pourable paste Curing
system Misture curing
Density 1.25 g/ml
Shore-A hardness 35° (3sec-ISO868)
Application temperature range +5°c to +30°c
Temperature resistance -30°c to +90°c
Tack free time 60min (23°c, 50% R.H.)
Curing speed 2mm/day (23°c, 50% R.H.)
Elongation at break 300% (ISO 37)
E- Modulus at 100% 0.5Mpa (ISO 37)
Dilatation joints in industrial floors
Horizontal tile joints and filling of floor cracks
Horizontal joints in warehouses, factories, parkings, terraces, roof works, road works and tanks
Very easy application
Suitable for all climates
Bubble – free curing, no yellowing
Resist permanent deformation
Excellent resistance to abrasion
Exceptional resistance to water, UV-Rays, corrosive environments
Very good resistance to acids and petroleum-based hydrocarbons
Stays elastic after curing.
Method of use Surface preparation
Joint walls must be sound, clean, dry, and free from oil and grease. Curing compound residues and any other foreign matter must be thoroughly removed, install bond breaker to prevent bond at the base of joint.
Priming is not usually necessary. Most substrates only require priming if testing indicates a need or where sealant will be subjected to water immersion after cure.
New concrete must be minimum of 28 days old.
Substrates must be dry; application in wet or damp joints will cause bubbling of the material
FARCO LEVEL FLEX is a one component and requires no pre-blending. It should be used directly from the container.
For good performance, it is essential that the sealant is only bonded to the two facing sides of the joint to achieve this, install a backup material (closed cell polyethylene or open cell polyurethane foam).
Apply the sealant in a continuous operation making sure all air pockets or voids are eliminated. Tool the sealant with light pressure to spread the material against the joint surfaces.
This operation should be made with dry spatula before skin formation occurs.
Material: Immediately with solvent Hardened sealant: can only be removed mechanically Hands: soap and water
Curing FARCO LEVEL
FLEX requires no special curing.
Joint width should be 4 times the expected joint movement, the depth of the sealant should be ½ the width of the joint material. The maximum depth is 15 mm. Installation of FARCO LEVEL FLEX deeper than what is recommended can cause bubbling or incomplete curing of the material.
Minimum depth: 6mm
Maximum depth: 15mm
Minimum width: 6mm
Maximum width: 30mm
Meter per 600ml foil bag
M. liter per
Use only at temperatures above 4°c.
Avoid exposure to high levels of chlorine.
Avoid contact with alcohol and other solvent cleaners during cure.
Do not cure in the presence of curing silicone sealant.
Do not apply in or damp joints, as this can cause bubbling within the sealant.
Other product info
FARCO LEVEL FLEX is supplied in 600 ml foil bags.
FARCO LEVEL FLEX in dry condition at temperatures between 5°c to 30°c.
12 month in original closed packing
Safety and Handling Precautions
Apply the usual industrial hygiene.
Prevent contact with skin, eyes or clothing. Wash thoroughly after handling. Do not take internally.
The SHIMISAKHTEMAN Technical Service Department is available to assist you in the correct use of our products in the field.
https://en.shimisakhteman.net/wp-content/uploads/2019/01/pic-product4.png300200adminhttp://shimisakhteman.net/wp-content/uploads/2019/01/logonahaee2-300x82.pngadmin2020-03-17 22:51:342020-03-17 22:51:34FARCOFLEX PRIMER
Office Address: No. 242, First floor, Mirdamad Blvd, Tehran, Iran
Contact Number: +98-21-27427
Factory address: East third and second, Simin Dasht Industrial Town, Shahriar Road, Karaj, Iran.
Contact number: +98-26-36670012-3-4
The company has been operating since 1972 under the management of Massoud Honarmand. Shimisakhteman holds a production license from the Ministry of Industry, Mining and Trade and has a mandatory standard certification of 2930. We have been selected as a standard sample unit every year since the 90’s.